Is 1161 301d47

IS1161:1998

STEEL TUBES FOR STRUCTURAL PURPOSES SPECIFICATION ( Fourth Revision ) First Reprint NOVEMBER 1998

ICS 77.140.75 ; 91.220

Q BIS 1998

BUREAU OF INDIAN STANDARDS MANAKBHAVAN, 9 BAHADUR SHAH ZAFAR MARG NEW Junuary

1998

DELHI

110002 Price Group 3

Steel Tubes, Pipes and Fittings Sectional Committee, MTD 19

FOREWORD This Indian Standard ( Fourth Revision ) was adopted by the Bureau of Indian Standards, after the draft finalized by the Steel Tubes, Pipes and Fittings Sectional Committee had been approved by the Metallurgical Engineering Division Council This standard was first published in 1958 and its first, second and third revisions were issued in 1963. 1968 and 1979 respectively. While reviewing the standard, the Committee has felt it necessary to revise this Indian Standard with the following modifications: a) Thickness andmass

is aligned with IS 1239 (Part 1) : 1990.

b) All amendments have been incorporated. In the formulation of this standard, due consideration has been given to the trade practices followed in the country in this field. Due consideration has also been given to international co-ordination among the standards prevailing in different countries. Assistance has been derived from the following publications: ISO/R 336 : 1976 Plain end steel tubes, welded or seamless; general table of dimensions and masses per unit length. International Organization for Standardization. BS 6323 : 1982 Steel tubes for-mechanical and general engineering purposes. British Standards Institution. This standard contains clauses 8.1 and X2.1which call for agreement between the purchaser and the manufacturer. For the purpose of deciding whether a particular requirement of this standard is complied with, the final value, observed or calculated, expressing the result of a test or analysis, shall be rounded off in accordance with IS 2 : 1960 ‘Rules for rounding off numerical values (revised)‘. The number of significant places retained in the rounded off value should be the same as that of the specified value in this standard.

IS 1161 : 1998

Indian Standard

STEEL TUBES FOR STRUCTURAL PURPOSES SPECIFICATION -(-Fourth Revision ) 1 SCOPE This standard covers the requirements for hot finished welded (HFW), hot finished seamless @IFS), and electric resistance welded (ERW) or high frequency induction welded (HRIW) plain carbon steel tubes for structural purposes.

as ‘Light’, ‘Medium’ and ‘Heavy’ depending on the wall thickness (see Table 1). They shall be further graded as Y St 2 10, Y St 240 and Y St 3 10 depending on the yield stress of the material (see Table 2). The designation of the steel tubes shall, therefore, include the nominal bore ofthe tube, classification on wall thickness and grade of the material.

2 REPERENCES

4 SUPPLY OF MATERIAL

The Indian-Standards listed below are the necessary adjuncts to this standard: IS No.

Title

228 : 1983

Method of chemical analysis of steel (in various parts)

1239 (Part 1) : 1990

Mild steel tubes, tubulars and other wrought steel fittings: Part 1 Mild steel tubes (#ifth revision)

1387: 1993

General requirements for the supply of metallurgical material (second revision)

1608: 1995

4.1 General requirements relating to the supply of the steel tubes for structural purposes shall conform to IS 1387. 5 MATERIAL 5.1 The tubes shall be manufactured from steel as given in Table 3 and shall be supplied in the conditions as shown therein. 6 DIMENSIONS AND WEIGHTS 6.1 The standard sizes and weights of tubes for structural purposes shall be as given in Table 1.

Mechanical testing of metals Tensile testing

6.1.1 Some geometrical properties of the steel tubes

2328: 1983

Method for flattening test on metallic tubes #rst revision)

6.1.2 Tubes of thickness lower than light tubes, specified in Table 1 shall not be permissible.

2329: 1985

Method for bend test on metallic tubes (in full section) (fwst revision)

4711: 1974

6.2 Tolerances The following tolerances shall apply:

Methods for sampling of steel pipes, tubes and fittings (first revision)

4736: 1986

Hot-dip zinc coatings on mild steel tubes (jkst revision)

4740 : 1979

Code of practice for packaging of steel tubes @rst revision)

10748 : 1995

are also given in Table 1 for information.

a) Outside Diameter: 1) Up to and including 48.3 mm

2)Gver48.3mm

+0.4mm _ o, 8 _ f 1.Opercent

b) Thickness flor all sizes): 1) Welded tubes

Hot-rolled steel strip for welded tubes and pipes yirst revision)

2) Seamless tubes

3 DESIGNATION

+ Not limited - 10 percent + Not limited - 12.5 percent

cl Weight:

3.1 Steel tubes covered by this standard shall be

1) Single tube light

designated by their nominal bore and shall be calssified 1

+ 10 percent - ~8 percent

B

Table 1 Sizes and Properties of Steel ‘hbes for Structural Purposes

5

Y ..

(Clauses3.1,6.1,6.1.1and6.1.2) Nominal Bore

Outside Diameter

mm (1)

mm (2)

15

21.3

20

25

26.9

33.7

Thickness

Weight

Area of Cross Section

Internal Volume

cm’ (6)

cm3/m

Surface External

Internal

cm3/m (8)

cm3/m

Moment of Inertia

Modulus of Section

Radius of Gyration

2

3

4

Square of Radius of Gyration

(3)

mm (4)

kg/m (5)

Light Medium Heavy

2.0 2.6 3.2

0.947 1.21 1.44

1.21 1.53 1.82

235 203 174

669

543 506 468

0.57 0.69 0.75

0.54 0.64 0.70

0.69 0.66 0.55

0.47 0.44 0.42

Light Medium Heavy

2.3 2.6 3.2

1.38 1.56 1.87

1.78 1.98 2.38

390 370 330

845

700 681 644

1.36 1.48 1.70

1 .Ol 1.10 1.26

0.87 0.86 0.84

0.76 0.74 0.71

Light Medium Heavy

2.6 3.2 4.0

1.98 2.41 2.93

2.54 3.06 3.73

638 585 518

1 059

895 857 807

3.09 3.61 4.19

1.83 2.14 2.48

1.10 1.08 1.05

1.21 1.17 1.11

Light Medium Heavy

2.6 3.2 4.0

2.54 3.10 3.79

3.25 3.94 4.82

1 086 1 017 929

1 332

1 168 1 130 1 080

6.47 7.62 8.99

3.05 3.59 4.24

1.41 1.39 1.36

1.98 1.93 1.86

Light Medium Heavy

2.9 3.2 4.b

3.23 3.56 4.37

4.13 4.53 5.56

1 418 1 378

1 517

1 335 1 316 1 265

10.70 11.59 13.77

4.43 4.80 5.70

1.61 1.59 1.57

2.59 2.54 2.41

Light Medium Heavy

2.9 3.6 4.5

4.08 5.03 6.19

5.23 6.41 7.88

1 711 1 667 1 611

21.59 25.88 30.90

7.16 8.58 10.2

2.03 2.00 1.98

4.13 4.02 3.92

Light Medium Heavy

3.2 3.6 4.5

5.71 6.42 7.9j

7.32 8.20 10.1

3 814 3 727

12.82 14.20 17.1

2.58 2.57 2.54

6.66 6.60 6.43

Light Medium Heavy

3.2 4.0 4.8

6.72 8.36 9.90

8.61 10.7 12.7

5 343 5 138 4 936

Light Medium Heavy

3.6 4.0 4.8

8.70 9.63 11.5

11.1 12.3 14.6

6 995 6 877

(7)

(9)

(“;“o,

(“1”)

(“II,

N

32

40

50

65

80

90

42.4

48.3

60.3

76.1

88.9

101.6

1 275 2 332 2 213 2 066

2 391

3 534

6 644

2 189 2 163 2 107 2 591

2 793

3 192

48.79 54.02 65.12

2 540 2 490

96.36 112.52

17.82 21.68 25.31

3.03 3.00 2.98

9.19 9.00 8.88

2 964 2 939

133.27 146.32 171.44

26.23 28.80 33.75

3.41 3.45 3.43

12.03 11.91 11.76

2 889

751.23

g

100

110

125

135

150

150

114.3

127.0

139.7

152.4

165.1

168.3

w 175

200

193.7

219.1

Light Medium Heavy

3.6 4.5 5.4

9.75 12.2 14.5

12.5 15.5 18.5

9 004 8 704 8 409

3 591

3 363 3 306 3 250

192.03 234.3 274.5

33.60 41.0 48.0

3.92 3.89 3.85

15.36 15.10 14.86

Light Medium Heavy

4.5 4.8 5.4

13.6 14.5 16.2

17.3 18.4 20.6

10 930 10 819 10 599

3 990

3 705 3 686 3 649

325.3 344.58 382.0

51.2 54.27 60.2

4.33 4.32 4.30

18.78 18.69 18.52

Light Medium Heavy

4.5 4.8 5.4

15.0 15.9 17.9

19.1 20.3 22.8

13 410 13 287 13 043

4 389

4 104 4 085 4 047

437.2 463.44 514.5

62.6 66.35 73.7

4.78 4.77 4.75

22.89 22.76 22.58

Light Medium Heavy

4.5 4.8 5.4

16.4 17.5 19.6

20.9 22.2 25.0

16 142 16 008 15 740

4 788

4 503 4 484 4446

572.2 606.92 674.5

75.1 79.65 88.5

5.23 5.22 5.20

27.37 27.25 27.05

Light Medium

17.8 18.9 21.3

22.7 24.2 27.1

19 128 18 981 18690

5 187

HeaY

4.5 4.8 5.4

4 902 4 883 4 845

732.6 777.32 864.7

88.7 94.16 105.0

5.68 5.67 5.65

32.27 32.14 31.92

Light Medium Heavy 1 Heavy 2

4.5 4.8 5.4 6.3

18.2 19.4 21.7 25.2

23.1 24.7 27.6 32.0

19 921 19 771 19 473 19 030

777.2 824.78 917.7 1 053

92.4 98.01 109.0 125.0

5.79 5.78 5.76 5.73

33.56 33.42 33.21 32.85

Light Medium H=T

4.8 5.4 5.9

22.4 25.1 27.3

28.5 32.0 34.8

26 606 26 260 25 974

6 085

5 781 5 743 5 712

1271.71 1 417 1 535.2

131.31 146 158.65

6.68 6.66 6.64

44.63 44.36 41.11

Light Medium Heavy

4.8 5.6 5.9

25.4 29.5 31 .o

32.3 37.5 39.5

34 454 33 930 33 734

6 883

6 578 6 528 6 509

1 856.51 2 141 2 247

169.47 195 205

7.58 7.55 7.54

57.45 57.02 56.86

5 287

5 4 4 4

002 983 946 889

225

244.5

Heavy

5.9

34.7

44.2

42 507

7 681

7 307

3 149

258

8.44

71.21

250

273.0

Heavy

5.9

38.9

49.5

53 557

8 578

8 202

4 412

323

9.45

89.30

300

323.9

Heavy

6.3

49.3

62.8

76 073

10 177

9 775

7 992

493

11.2

125.44

350

355.6

Heavy

8.0

68.6

87.3

90 533

11 173

10 663

13 111

737

12.3

151.29 t:

IS 1161 : 1998 Medium

the values specified for the relevant grades of tubes given in Table 2.

f 10 percent Heavy

11.2.1 The tensile test shall be made on:

2) 10 tonne lots light

l

5 percent

a) a length cut from the end of the selected tube (the ends of the length being plugged for grips, where necessary); or

Medium f 7.5 percent Heavy

j

b) a longitudinal strip cut from the tube, not including the weld, ifany, and tested in the curved condition, the choice resting with the manufacturer.

NOTE - For 10 tonne lots, the weighment may-be done in convenient smaller lots and added up at the option of the manufacturer.

7 woRKMANsHIP

Table 2 Tensile Properties of Steel ‘lhbes for Structural Purposes

7-l The tubes shall be cleanly finished and reasonably free from scale. They shall be free from cracks, surface flaws, laminations and other defects. The ends shall be cut cleanly and square with the axis of tube, unless otherwise specified.

( Clauses 3.1 and 11.2 ) Tensile Strength (Min)

Grade

Surface imperfections such as handling marks, light die or ~011 marks, or shallow pits shall not be considered as defects provided the imperfections are removable within minimum wall thickness permitted. Removal of such surface imperfections is not required. Welded tubing shall be free of protruding metal on the outside surface of the weld seam.

Yst 2~10 YSt 240 Yst 310

Yield Stress (Min)

Elongation on Gxuge Length 5.65 \iS, Min

MPa

MPa

Percent

330 410 450

210 240 310

20 17 14

NOTES 1 1 MPa = lN/mml= 0.102 kgflmm’ 2 Elongation percent for tubes up to and including

8 GAW.ANIZING

25 mm nominal bore for all grades shall be 12 mmimum.

8.1 If the tubes are required in galvanized condition the zinc coating on the tubes shall be conforming to the requirements and tested as per methods, specified in IS 4736.

Table 3 Steel and Supply Conditions ( Clause 5.1) Sl

9 STRAIGHTNESS

No.

9.1 Unless otherwise agreed to between the purchaser and the manufacturer, tubes shall not deviate from straightness by more than 1 mm in any 600 mm length.

Manufacturing Process

Only YSt 210 or YSt 240

ii) HFS

with Bars/ingots chemical suitable composition as per IS 10748 to achieve mechanical proper ties .for respective grades

YSt 210, YSt 240 or YSt 310

iii) ERW/HRIW

IS 10748

YSt 210, YSt 240 or YSt 310 as heat welded,

HPW

10 LENGTHS 10.1 The tubes shall normally be supplied in random lengths at 4 to 7 m. If ordered in exact lengths, the tolerances shall be subject to prior agreement between the manufacturer and the purchaser.

11.1 The following tests shall be carried out on the selected tube, strip or plate. For mechanical tests, tubes shall be sampled in accordance with IS 47 11.

SUPPlY Conditions

IS 10748

i)

11 MECHANICALTESTS

Steel

treated or cold and drawn normalized NOTE - If required the copper bearing steel may be used to impart weather resistant properties in the steel. Copper content shall be between 0.20 to 0.35 percent

11.2 Tensile Test The tensile strength, the yield stress and the percentage elongation shall be determined in accordance with the methods specifiedin IS 1608 and shall be not less than

subject to mutual agreement between the supplier and the purchaser.

4

IS 1161 : 1998 11.3 Ductility Test

11.5 Sampling

11.3.1 Cold Bend Test ( Up to and Including 50 mm NB)

11.5.1 Sampling ofTubes For the purpose of drawing samples all mild steel tubes bearing same designation and manufactured under a single process shall be grouped together to constitute a lot. Each lot shall be sampled separately and assessed for conformity to this specification.

When tested in accordance with IS 2329 an unfilled length of tube shall be capable of being bent cold by tube bending machine around a grooved former (with radius at bottom of the groove equal to 6 x 0. D. of the tube) through 180” (with weld at 90” to the plane of bending) without showing any crack at the weld or themetal.

11.5.2 Sampling and Criterion for Conformity Unless otherwise agreed to between the manufacturer and the purchaser the procedure for sampling of tubes for various tests and criteria for conformity shall be asgiven in IS 47 11.

11.3.2 Flattening Test ( TubesAbove 5Omm NB ) Rings, not less than 40 mm in length cut from the ends of selected tubes with edges rounded shall be flattened between parallel plates with the weld, if any, at 90“ (point of maximum bending) in accordance with IS 2328. No opening shall occur by fracture in the weld until the distance between the plates is less than the value specified for each grade in co1 4 of Table 4 and no cracks or breaks in the metal elsewhere than in the weld shall occur until the distance between the plates is iess than the value specified for each grade incol5 ofTable4.

12 MARKING 12.1 Each tube shall be suitably marked with the manufacturer’s name or trade-mark, and class of the tube. 12.1.1 The tubes may also be marked with the Standard Mark. 12.1.2 The use of the Standard Mark is governed by the provisions of the Bureau of Indian Standards Act, 1986 and the Rules and Regulations made thereunder. The details of conditions under which~the licence for the use of Standard Mark may be granted to manufacturers or producers may be obtained from the Bureau of Indian Standards.

11.4 Retest Should any one of the test pieces first selected fail to any of the tests specified, two further samples shall be selected for testing in respect of each failure from the same lot. Should the test pieces from both these additional samples, the material represented by the test samples shall be deemed to comply with the requirement of that particular test. Should the test pieces from either of these additional samples fail, the material represented by the test samples shall be deemed as not complying with the standard or the manufacturer may select to test individually the remaining lengths in the lot for the test failed to comply in the preceding tests.

13 OILINGANDPAINTING 13.1 All tubes shall, unless otherwise specified, bc varnished, painted or oiled externally. 14 BUNDLING AND PACKING 14.1 Where tubes are to be bundled for transport, they shall unless otherwise specified, be packed in accordance with IS 4740.

Table 4 Flattening Requirement in Metal (Clause 11.3.2) Sl

Manufacturing

Process

Metal

Steel

Grade

NO.

Weld

Parent

(Distance Between the Plates)

(Distance between the Plates)

i)

HFWIHFSIERWIHFIW

Yst 210

75 percent of 0.D.”

60 percent of 0.1).

ii)

HFWIHFSIERWIHFIW

YSt 240

85 percent of O.D.

75 percent of 0.11.

~FHS/ERW/HFIW

Yst 310

85 percent of O.D.

75 percent of O.D.

iii)

I) O.D. = Outside diameter.

5

Bureau of Indian Standards BIS is a statutory institution established under the Bureau oflndian Standards Act, 1986 to promote harmonious development of the activities of standardization, marking and quality certification of goods and attending to connected matters in the country. Copyright BIS has the copyright of all its publications. No part of these publications may be reproduced in any form without the prior permission in writing of BIS. This does not preclude the free use, in the course of implementing the standard, of necessary details, such as symbols and sizes, type or grade designations. Enquiries relating to copyright be addressed to the Director (Publications), BIS. Review of Indian Standards Amendments are issued to standards as the need arises on the basis of comments. Standards are also reviewed periodically; a standard along with amendments is reaffirmed when such review indicates that no changes are needed; if the review indicates that changes are needed, it is taken up for revision. s of Indian Standards should ascertain that they-are in possession of the latest amendments or edition by referring to the latest issue of ‘BlS Handbook’ and ‘Standards : Monthly Additions’. This Indian Standard has been developed from Dot : No. MTD 19 ( 4099 ). Amendments Issued Since Publication Amend No.

Text Affected

Date of Issue

BUREAU

OF

INDIAN

STANDARDS

-Headquarters: Manak-Bhavan, 9 Bahadur Shah Zafar Marg, New Delhi 110002 Telephones : 323 01 31, 323 94 02, 323 33 75 Regional Offices: Central : Manak Bhavan, 9 Bahadur Shah Zafar Marg NEW DELHI 110002 Eastern : l/14 C. I. T. Scheme VII M, V. I. P. Road, Maniktola CALCUTTA 700054 Northern : SC0 335-336, Sector 34-A, CHANDIGARH 160022 Southern : C. I. T. Campus, IVCross Road, CHENNAI 600113 Western : Manakalaya, E9 MIDC, Marol, Andheri (East) MUMBAI 400093

Telegrams: Manaksanstha ( Common to all offices ) Telephone 323 76 17 323384: 337 84 99,331 337 86 26, 337 I 60 I 60

85 61 86 62 38 43 20 25

235 02 16,235 04 42 235 15 19,235 23 15 832 92 95,832 78 58 I 8327891,8327892

BHUBANESHWAR. BHOPAL. BANGALORE. Branches : AHMADABAD. COIMBATORE. FARIDABAD. GHAZIABAD. GUWAHATI. HYDERABAD. JAIPUR. KANPUR. LUCKNOW. NAGPUR. PATNA. PUNE. THIRUVANANTHAPURAM.

Printed at New India Printing Press, Khwja, Indm

AMENDMENT

NO. 1 MARCH 2000 TO IS 1161 : 1998 STEEL TUBES FOR STRUCTURAL PURPOSES - SPECIFICATION (Fourth ( Pqe 5, clause 12.1, ‘trade-mark’.

line 2 ) -

Revision) Insert ‘grade of the steel’ after the words

(MTD 19) Reprography Unit, BE, New Delhi, India